- The dsc curve and xrd of vo xerogel revealed that three - change process during the drying process of xos sol
- The peo - v2o5 - moo3 xerogel thin films show the excellent cycling reversibility and stability of li + ions insertion / extraction in the interlayer of v2o5 - moo3 xerogel
- The surface structure of sample a would be more regulate and complete than sample b after annealing . tga was applied to analyze the weight loss process of vio xerogel
- The sem micrographs of xerogel thin films show that the surface of the films is homogeneous , no cracks and holes are observed and it has a fiber - like microstructure
- The major results were listed below : the forming processing of xos xerogel was studied . the results showed that it is useful to apply the oxygen top - blend technique to the fabrication of vaos xerogel by melt quenching
- The synthesis of water - soluble pyrrole and poly ( trimethyl - ( 2 - pyrrol - l - yl - ethyl ) - ammonium iodide ) / vios nanocomposite was studied systemically . the vos xerogel was prepared by melt quenching method and the fabrication method was improved
- Peo can be completely intercalated into the interlayer of v2o5 xerogel in form of amorphous state at x = 0 . 5 , whereas partial peo can not be intercalated into v2os xerogel interlayer and exists outside of v2o5 xerogel interlayer in form of crystalline state at x = l , 2
- Peo can be completely intercalated into the interlayer of v2o5 - moo3 xerogel in form of amorphous state at x 1 , whereas partial peo can not be intercalated into v2o5 - moo3 xerogel interlayer and exists outside of v2o5 - moo3 xerogel interlayer in form of crystalline state at x = 2
- The xps analyses show that there were two different chemical conditions of li + ions when li + ions were inserted into v2o5 - moo3 xerogel , corresponding to the li + ions in the interlayer and interstitial positions ( localized by the layers ) of v2o5 - moo3 lattice , respectively
- During the temperature of 360410 , the weight lose was aboutl . 8 % of both sample a and sample b . the calculating result of n ( water molecular number ) was n = 1 . 59 ( sample a ) , n = 1 . 79 ( sample b ) respectively . li + ion storage properties in xos xerogel films were related to the content of v5 + ion and the situation number that li + ion were capable to hold
- The stretching vibration of v = o shifts to lower wavenumbers , which is contributed to the oet v : = o bonding interaction . the intercalation of peo effectively shields the electrostatic interaction between li + ions and v2o5 layers , resulting in the improvement of the cycling reversibility and stability of li + ions insertion / extraction in the interlayer of v2o5 xerogel and the improvement of electrochromic behavior of the films
- In this thesis , based on organic aerogel and porous silicon ( ps ) that are two types of materials in frontier field of materials science , carbon aerogel , carbon xerogel and free - standing porous silicon films were prepared and used as the anode materials for lithium ion batteries , and their performance of lithium ion storage and behavior of charge and discharge were studied . meanwhile , the effects of synthetic conditions on their performance as anode materials were also analysed
- ( 1 ) carbon aerogel and xerogel were made from resorcinol - formaldehyde organic gels and used as the anode materials for lithium ion batteries . by discussing the influences of pyrolysis temperature , the level of the catalyst and the concentration of reactant in the preparation of carbon materials on their behavior of lithium ion storage , their performance of storing lithium ions and process of charge and discharge were studied in details . moreover , the relationship between the structure of carbon aerogel and xerogel and the performance of storing lithium ions was analysed , and the mechanism of the storage of lithium ions in this type of porous carbon materials based on organic gels was also dicussed simply
- Two kinds of n - substituted pyrrole ( trimethyl - ( 2 - pyrrol - l - yl - ethyl ) - ammonium iodide and 2 - ( 2 - pyrrol - 1 - yl - ethoxy ) - ethane - sulfonate sodium ) were synt hesized ; poly ( trimethyl - ( 2 - pyrrol - l - yl - ethyl ) - ammonium iodide ) / v2os nanocomposites were synthesized by two methods ( monomer in - situ intercalate polymerization and polymer intercalation in solvent ) . to fabricate vaos sol by melt quenching , oxygen top - blend technique was applied to improve oxygenic part - pressure , decrease the oxygenic anoxic and restrain the increase of v4 + ion when vos was melted . the xos xerogel prepared by the new technique had more complete structure than the vos xerogel which v20s powder was melted in the air